D2 tool steels
Related Product Searches:D2 tool steels,High Quality D2 tool steels,D2 tool steels 1.2379 D2 SKD11,Cr12Mo1V1
D2 tool steels: 1.good service 2.quality guarantee 3.competitive price
USAGE: Applied in thickness no less than 2mm punch mould, all kind of small mould for shearing and cutter together with screw0rolled or slappered mould as well as some other forming mould like rulers..
CHARACTERISTIC: E.S.R. materials, high compression strength and fine robustness. The spherical annealed make it easily processed by shearing and cutting with no crake while processing.
SIMILAR STEEL GRADE:
standard | GB | JIS | ASTM | DIN | ISO |
Steel grade | Cr12Mo1V1 | SKD11 | D2 | 1.2379 | 160CrMoV12 |
CHEMICAL COMPOSITION (%)
C | Mo | Mn | Cr | V | Si | S | P |
1.45-1.60 | 0.70-1.00 | 0.20-0.60 | 11.00-13.00 | 0.70-1.00 | 0.10-0.60 | ≤0.030 | ≤0.030 |
HARDNESS:≤255HB
DELIVERY STATUS: In annealed condition.
HEAT TREATMENT CONDITION:
1) Quenching temperature: 1000--1040°C
Cooling Medium: oil-cooling or air-cooling
Tempering temperature: 180-200°C, by two times
Tempering Hardness: ≥63.0HRC
2) Quenching temperature: 1060--1080°C
Cooling Medium: oil-cooling or air-cooling
Tempering temperature: 500-540°C, by two times
Tempering Hardness: ≥59.0-61.0HRC
D2 Tool Steel: 1.good service 2.quality guarantee 3.competitive price
USAGE: Applied in thickness no less than 2mm punch mould, all kind of small mould for shearing and cutter together with screw0rolled or slappered mould as well as some other forming mould like rulers..
CHARACTERISTIC: E.S.R. materials, high compression strength and fine robustness. The spherical annealed make it easily processed by shearing and cutting with no crake while processing.
SIMILAR STEEL GRADE:
standard | GB | JIS | ASTM | DIN | ISO |
Steel grade | Cr12Mo1V1 | SKD11 | D2 | 1.2379 | 160CrMoV12 |
CHEMICAL COMPOSITION (%)
C | Mo | Mn | Cr | V | Si | S | P |
1.45-1.60 | 0.70-1.00 | 0.20-0.60 | 11.00-13.00 | 0.70-1.00 | 0.10-0.60 | ≤0.030 | ≤0.030 |
HARDNESS:≤255HB
DELIVERY STATUS: In annealed condition.
HEAT TREATMENT CONDITION:
1) Quenching temperature: 1000--1040°C
Cooling Medium: oil-cooling or air-cooling
Tempering temperature: 180-200°C, by two times
Tempering Hardness: ≥63.0HRC
2) Quenching temperature: 1060--1080°C
Cooling Medium: oil-cooling or air-cooling
Tempering temperature: 500-540°C, by two times
Tempering Hardness: ≥59.0-61.0HRC